PEMBUATAN NANOFLUIDA Al2O3 DARI NANOPARTIKEL Al2O3 HASIL SINTESIS MENGGUNAKAN METODE SOL GEL DENGAN TEPUNG TAPIOKA SEBAGAI CAPPING AGENT UNTUK APLIKASI DI RADIATOR

Diki Yuliardi, - (2020) PEMBUATAN NANOFLUIDA Al2O3 DARI NANOPARTIKEL Al2O3 HASIL SINTESIS MENGGUNAKAN METODE SOL GEL DENGAN TEPUNG TAPIOKA SEBAGAI CAPPING AGENT UNTUK APLIKASI DI RADIATOR. S1 thesis, Universitas Pendidikan Indonesia.

Abstract

Pembuatan nanofluida air-Al2O3 dari nanopartikel Al2O3 hasil sintesis menggunakan metode sol gel dengan tepung tapioka sebagai capping agent untuk aplikasi di radiator telah dilakukan. Nanofluida air-Al2O3 disintesis menggunakan metode dua langkah (Two step method) dengan dua konsentrasi berbeda yaitu 0,1 %wt dan 0,2 %wt. Pengujian heat transfer pada penelitian ini menggunakan set alat radiator dengan menjaga tetap laju aliran fluida dan suhu inlet sebesar 3,3 LPM (liter/menit) dan 50oC. Serbuk nanopartikel Al2O3 dikarakterisasi menggunakan X-ray diffraction (XRD) dan Surface Area Meter. Hasil karakterisasi XRD menunjukkan nanopartikel Al2O3 yang telah disintesis merupakan alpha-Al2O3. Ukuran kristal dan ukuran partikel nanopartikel Al2O3 sebesar 36,25 nm dan 80,47 nm. Potensial zeta nanofluida air-Al2O3 yang dihasilkan sebesar -35,26 mV dan -37,83 mV untuk konsentrasi 0,1 %wt dan 0,2 %wt. Penambahan konsentrasi pada nanofluida meningkatkan heat transfer pada radiator. Convective Heat Transfer Coefficient dan Overall Heat Transfer Coefficient masing-masing meningkat sebesar 139,52% dan 168,31% dibandingkan air sebagai fluida dasar. Fabrication of water-Al2O3 nanofluids from Al2O3 nanoparticles synthesized using sol gel method with tapioca starch as capping agent for application in radiator were succesful. Water-Al2O3 nanofluids synthesized with two step method with two different concentration 0,1 %wt and 0,2 %wt. Heat transfer test in this study using radiator machine with constant fluids flow and inlet temperature with 3,3 LPM (liter/minute) and 50oC. The powder of Al2O3 nanoparticles were characterization with X-ray diffraction (XRD) and Surface Area Meter. The result of XRD analysis show Al2O3 nanoparticles was synthesized is alpha-Al2O3. Crystallize and particle size of Al2O3 nanoparticles was 36,25 nm and 80,47 nm. Zeta potential of water-Al2O3 nanofluids was -35,26 mV and -37,83 mV for Al2O3 concentrations of 0,1 %wt and 0,2 %wt. Addition of concentration of nanofluids increases heat transfer of radiator. Convective Heat Transfer Coefficient and Overall Heat Transfer Coefficient increases up to 139,52% and 168,31% compared with water as base fluids.

Baca Full Text klik disini
[img] Text
S_FIS_1403489_Title.pdf
Download (505kB)
[img] Text
S_FIS_1403489_Chapter1.pdf
Download (122kB)
[img] Text
S_FIS_1403489_Chapter2.pdf
Restricted to Staf Perpustakaan
Download (622kB)
[img] Text
S_FIS_1403489_Chapter3.pdf
Download (724kB)
[img] Text
S_FIS_1403489_Chapter4.pdf
Restricted to Staf Perpustakaan
Download (427kB)
[img] Text
S_FIS_1403489_Chapter5.pdf
Download (207kB)
[img] Text
S_FIS_1403489_Appendix.pdf
Restricted to Staf Perpustakaan
Download (604kB)
Official URL: http://repository.upi.edu
Item Type: Thesis (S1)
Additional Information: No Panggil : S FIS DIK p-2020; NIM : 1403489
Uncontrolled Keywords: Nanofluida, Nanopartikel, Al2O3, Tepung Tapioka, Convective Heat Transfer Coefficient, Overall Heat Transfer Coefficient
Subjects: L Education > L Education (General)
Q Science > QC Physics
Divisions: Fakultas Pendidikan Matematika dan Ilmu Pengetahuan Alam > Program Studi Fisika - S1 > Program Studi Fisika (non kependidikan)
Depositing User: Diki Yuliardi
Date Deposited: 15 Sep 2020 01:57
Last Modified: 15 Sep 2020 01:57
URI: http://repository.upi.edu/id/eprint/53175

Actions (login required)

View Item View Item