Azhar, Diana (2015) PENGARUH PENAMBAHAN ABU VULKANIK TERHADAP KUAT TEKAN BETON SCC. S1 thesis, Universitas Pendidikan Indonesia.
|
Text
S_TS_1002543_Title.pdf Download (81kB) | Preview |
|
|
Text
S_TS_1002543_Abstract.pdf Download (134kB) | Preview |
|
|
Text
S_TS_1002543_Table_of_content.pdf Download (209kB) | Preview |
|
|
Text
S_TS_1002543_Chapter1.pdf Download (278kB) | Preview |
|
![[img]](http://repository.upi.edu/style/images/fileicons/text.png) |
Text
S_TS_1002543_Chapter2.pdf Restricted to Staf Perpustakaan Download (682kB) |
|
|
Text
S_TS_1002543_Chapter3.pdf Download (528kB) | Preview |
|
|
Text
S_TS_1002543_Chapter4.pdf Restricted to Staf Perpustakaan Download (1MB) |
|
|
Text
S_TS_1002543_Chapter5.pdf Download (197kB) | Preview |
|
|
Text
S_TS_1002543_Appendix.pdf Restricted to Staf Perpustakaan Download (4MB) |
Abstract
Beton SCC terus dikembangkan sebagai alternative dalam pelaksanaan pengecoran beton. Beton SCC merupakan beton yang mampu mengalir dibawah beratnya sendiri dengan slump yang tinggi serta mampu mengisi ruang cetakan tanpa mengalami segregasi dan mencapai kepadatan tertinggi. Untuk menghasilkan beton SCC diperlukan bahan tambah (adimixture) untuk melengkapi kinerja semen. Seuperplasticizer bahan tambah yang digunakan dengan jenis ADVA 455 sebesar 1,5% dari berat semen. Penelitian ini dilakukan untuk mengetahui pengaruh abu vulkanik terhadap kuat tekan beton SCC. Pengujian meliputi passing ability test, segregation resistance test, filling ability test dan kuat tekan beton pada umur 3, 7, 14, dan 28 hari. Variasi penambahan abu vulkanik yaitu 2%, 4%, 6% dan 8% dari berat semen.penambahan abu vulkanik berpengaruh terhadap workability dan kuat tekan beton. Kuat tekan tertinggi pada penambahan abu vulkanik sebesar 4% dengan hasil kuat tekan pada umur 28 haru sebesar 50,70 MPa, sedangkan hasil kuat tekan terendah pada penambahan abu vulkanik sebesar 8% dengan kuat tekan 43,70 MPa.---------- SCC Concrete being developed as an alternative in the implementation of concrete foundry. SCC is concrete that be able to flow under its own weight with high slump and able to fill the mold space without condition segregation and achieve the highest density. To produce SCC additional material (admixture) to complete performance of the cement. Additional materials used is superplasticitizer with ADVA 455 kinds of 1.5% of the weight of the cement. This study was conducted to determine the effect of volcanic ash on the compressive strength of SCC. Testing includes passing ability test, segregation resistance test, filling ability test and compressive strength of concrete at the age of 3, 7, 14, and 28 days. Variations addition of volcanic ash that is 2%, 4%, 6% and 8% by weight of cement. The addition of volcanic ash affect the workability and compressive strength of concrete. The highest compressive strength occurs upon the addition of volcanic ash by 4% with the results of compressive strength at age 28 amounted 50.70 MPa, while the lowest occurred compressive strength results in the addition of volcanic ash by 8% with a compressive strength of 43.70 MPa.
| Item Type: | Thesis (S1) |
|---|---|
| Additional Information: | No. Panggil : S TS AZH p-2015 ; Pembimbing : I.Nanang Dalil Heman, II. Ben Novaro Batubara |
| Uncontrolled Keywords: | Beton SCC, Admixture, superplasticizer, abu vulkanik , kuat tekan |
| Subjects: | T Technology > TH Building construction |
| Divisions: | Fakultas Pendidikan Teknologi dan Kejuruan > Jurusan Pendidikan Teknik Sipil > Program Studi Teknik Sipil |
| Depositing User: | Mr. Tri Agung |
| Date Deposited: | 02 Sep 2016 02:49 |
| Last Modified: | 02 Sep 2016 02:49 |
| URI: | http://repository.upi.edu/id/eprint/22104 |
Actions (login required)
 |
View Item |