PENGARUH PROSES POWDER NITRIDING TERHADAP PERUBAHAN KEKERASAN DAN TEBAL LAPISAN DIFUSI PADA PAHAT BUBUT HIGH SPEED STEEL

Rahayu, Sri (2017) PENGARUH PROSES POWDER NITRIDING TERHADAP PERUBAHAN KEKERASAN DAN TEBAL LAPISAN DIFUSI PADA PAHAT BUBUT HIGH SPEED STEEL. S1 thesis, Universitas Pendidikan Indonesia.

[img]
Preview
Text
S_FIS_1103178_Title.pdf

Download (120kB) | Preview
[img]
Preview
Text
S_FIS_1103178_Abstract.pdf

Download (204kB) | Preview
[img]
Preview
Text
S_FIS_1103178_Table_of_content.pdf

Download (140kB) | Preview
[img]
Preview
Text
S_FIS_1103178_Chapter1.pdf

Download (141kB) | Preview
[img] Text
S_FIS_1103178_Chapter2.pdf
Restricted to Staf Perpustakaan

Download (620kB)
[img]
Preview
Text
S_FIS_1103178_Chapter3.pdf

Download (500kB) | Preview
[img] Text
S_FIS_1103178_Chapter4.pdf
Restricted to Staf Perpustakaan

Download (443kB)
[img]
Preview
Text
S_FIS_1103178_Chapter5.pdf

Download (195kB) | Preview
[img]
Preview
Text
S_FIS_1103178_Bibilography.pdf

Download (204kB) | Preview
[img] Text
S_FIS_1103178_Appendix.pdf
Restricted to Staf Perpustakaan

Download (747kB)
Official URL: http://repository.upi.edu

Abstract

Baja Kecepatan Tinggi (HSS) merupakan baja paduan tinggi dengan unsur paduan utama karbon (C), tungsten (W), vanadium (V), molybdenum (Mo), kromium (Cr) dan kobalt (Co). Material HSS banyak digunakan sebagai pahat pada mesin perkakas karena memiliki sifat keuletan yang relatif baik dan apabila telah aus pahat HSS masih dapat diasah sehingga mata potongnya menjadi tajam kembali. Pada penelitian ini untuk meningkatkan kinerja pahat HSS dilakukan dengan cara perlakuan permukaan (surface treatment) menggunakan teknik powder nitriding. Powder Nitriding merupakan proses perlakuan permukaan dengan menambahkan unsur nitrogen kedalam permukaan baja dengan menggunakan media padat berupa serbuk nitrida. Proses powder nitriding menggunakan temperatur 5600C dan 6000C dengan holding time 1 dan 3 jam. Media nitriding yang digunakan adalah urea dan cangkang kerang. Hasil pengujian menunjukkan bahwa : kekerasan permukaan tertinggi diperoleh pada suhu 560oC dengan holding time 1 jam yaitu sebesar 876,94 HV atau meningkat sebesar 22% dari raw material (720 HV). Hasil pengamatan struktur mikro kedalaman lapisan difusi tertinggi yang diperoleh yaitu sebesar 21 μm untuk suhu 560oC dengan holding time 3 jam. Pengujian EDS menunjukkan kandungan nitrogen hasil nitridasi pada variasi suhu 560oC dengan holding time 1 jam yaitu sebesar 3,08 % berat atau 11,08 % atom. ;---High Speed Steel is a high alloy steel with main alloy element of Carbon (C), Tungsten (W), Vanadium (V), Molybdenum (Mo), Chromium (Cr) and Cobalt (Co). HSS material is widely used as a chisel on machine tools because its relatively good ductility and when it becomes worn, HSS still can be sharpened for rause pupose. To improve the performance of HSS, research was done by conducting surface treatment using powder nitriding technique. powder nitriding is a surface treatment process with adding nitrogen elements to the steel surface using a solid medium of nitride powder. The powder nitriding processed by carried out temperatures 5600C and 6000C with 1 hour and 3 hours holding time . Nitriding medium consisted of urea and shellfish. Result showed that the highest surface hardness that obtained at temperature 560oC with 1 hour holding time was 876,94 HV or increased 22% from raw material (720 HV). Micro structure observed the depth of the highest diffusion layer obtained was 21 μm for the temperature 560oC with holding time 3 hours. EDS test result also showed that nitrogen content at 560oC with 1 hour holding time is 3.08% wt or 11.08% at.

Item Type: Skripsi,Tesis,Disertasi (S1)
Additional Information: No. Panggil : S FIS RAH p-2017; Pembimbing : I. Shinta Virdhian, II. Edi Suhendi; NIM : 1103178.
Uncontrolled Keywords: Powder Nitriding, Material HSS, kekerasan perumukaan, kedalaman lapisan difusi nitrogen, Powder Nitriding, HSS Material, Surface Hardness, Depth of Nitrogen Diffusion Layer.
Subjects: Q Science > QC Physics
Divisions: Fakultas Pendidikan Matematika dan Ilmu Pengetahuan Alam > Jurusan Pendidikan Fisika > Program Studi Fisika (non kependidikan)
Depositing User: Isma Anggini Saktiani
Date Deposited: 16 Mar 2018 06:31