PENGARUH SUHU PIROLISIS PADA PEMBUATAN ADSORBEN DAUN NANAS TERHADAP ADSORPSI METHYLENE BLUE MENGGUNAKAN AKTIVATOR NaCl

Mochamad Rois Nabhan, - and Dani Gustaman Syarif, - and Endi Suhendi, - (2025) PENGARUH SUHU PIROLISIS PADA PEMBUATAN ADSORBEN DAUN NANAS TERHADAP ADSORPSI METHYLENE BLUE MENGGUNAKAN AKTIVATOR NaCl. S1 thesis, Universitas Pendidikan Indonesia.

Abstract

Penggunaan biosorben telah menjadi solusi potensial dalam pengolahan limbah cair, khususnya untuk mengatasi pencemaran akibat logam berat, zat warna, dan senyawa organik. Namun, tantangan utama yang masih dihadapi adalah kapasitas adsorpsi biosorben yang relatif rendah dibandingkan adsorben sintetis, yang dipengaruhi oleh struktur pori dari material biosorben tersebut. Penelitian ini bertujuan untuk mengoptimalkan adsorpsi karbon aktif berbasis daun nanas melalui metode aktivasi menggunakan NaCl dan pirolisis pada variasi suhu 500°C, 600°C, dan 700°C, serta menganalisis pengaruhnya terhadap kristalinitas, morfologi, serta efisiensi dan kapasitas adsorpsi terhadap zat pewarna Methylene Blue (MB). Hasil penelitian menunjukkan bahwa efisiensi penyisihan tertinggi diperoleh pada suhu pirolisis 700°C dengan efisiensi sebesar 87,07% dengan 20 ml Methylene Blue, sedangkan kapasitas adsorpsi 42,27 mg/g dengan 60 ml Methlylene Blue. Sebaliknya, efisiensi terendah terjadi pada suhu 500°C dengan volume MB sebanyak 60ml yaitu sebanyak 30,15% dan kapasitas adsorpsi sebesar 18,09 mg/g. Sejalan dengan itu, karakterisasi struktur morfologis menunjukkan bahwa ketebalan rata-rata rongga pori biosorben juga meningkat seiring suhu aktivasi. Dengan demikian, dapat disimpulkan bahwa semakin tinggi suhu pirolisis, semakin besar efisiensi dan kapasitas adsorpsi karbon aktif yang dihasilkan. The use of biosorbents is a potential wastewater treatment solution for heavy metals, dyes, and organic compounds, though their adsorption capacity is often limited by pore structure compared to synthetic adsorbents. This study aimed to optimize pineapple leaf-based activated carbon adsorption using NaCl activation and pyrolysis at 500°C, 600°C, and 700°C, analyzing its impact on crystallinity, morphology, and Methylene Blue (MB) adsorption efficiency and capacity. Results showed the highest removal efficiency of 87.07% at 700°C (with 20 ml MB), yielding an adsorption capacity of 42.27 mg/g (with 60 ml MB). Conversely, the lowest efficiency was 30.15% at 500°C (with 60 ml MB), with a capacity of 18.09 mg/g. Morphological analysis confirmed that the average pore cavity thickness of the biosorbent increased with higher activation temperatures. Thus, the study concluded that increased pyrolysis temperature leads to greater efficiency and adsorption capacity of the resulting activated carbon.

	Text S_FIS_1908585_Title.pdf Download (514kB)
	Text S_FIS_1908585_Chapter 1.pdf Download (288kB)
	Text S_FIS_1908585_Chapter 2.pdf Restricted to Staf Perpustakaan Download (860kB) | Request a copy
	Text S_FIS_1908585_Chapter 3.pdf Download (1MB)
	Text S_FIS_1908585_Chapter 4.pdf Restricted to Staf Perpustakaan Download (2MB) | Request a copy
	Text S_FIS_1908585_Chapter 5.pdf Download (267kB)
	Text S_FIS_1908585_Appendix.pdf Restricted to Staf Perpustakaan Download (358kB) | Request a copy

Item Type:	Thesis (S1)
Additional Information:	Sinta ID Dosen Pembimbing: Dani Gustaman Syarif : 6051241 Endi Suhendi : 5976806
Uncontrolled Keywords:	Biosorben, Karbon aktif, Daun nanas , Methylene Blue, Adsorpsi Biosorbent, Activated carbon, Pineapple leaves, Methylene Blue, Adsorption
Subjects:	L Education > L Education (General) Q Science > QC Physics
Divisions:	Fakultas Pendidikan Matematika dan Ilmu Pengetahuan Alam > Program Studi Fisika - S1
Depositing User:	Mochamad Rois Nabhan
Date Deposited:	07 Aug 2025 02:43
Last Modified:	07 Aug 2025 02:43
URI:	http://repository.upi.edu/id/eprint/135248

Actions (login required)

View Item