SINTESIS NANOPARTIKEL MAGNETIK Fe3O4@Au DENGAN VARIASI KONSENTRASI HAuCl4 UNTUK APLIKASI SENSOR PENDETEKSI LOGAM BERAT

Revanya Debora, - (2024) SINTESIS NANOPARTIKEL MAGNETIK Fe3O4@Au DENGAN VARIASI KONSENTRASI HAuCl4 UNTUK APLIKASI SENSOR PENDETEKSI LOGAM BERAT. S1 thesis, Universitas Pendidikan Indonesia.

[img] Text
S_FIS_2009105_Title.pdf

Download (2MB)
[img] Text
S_FIS_2009105_Chapter1.pdf

Download (625kB)
[img] Text
S_FIS_2009105_Chapter2.pdf
Restricted to Staf Perpustakaan

Download (1MB)
[img] Text
S_FIS_2009105_Chapter3.pdf

Download (1MB)
[img] Text
S_FIS_2009105_Chapter4.pdf
Restricted to Staf Perpustakaan

Download (1MB)
[img] Text
S_FIS_2009105_Chapter5.pdf

Download (582kB)
[img] Text
S_FIS_2009105_Appendix.pdf
Restricted to Staf Perpustakaan

Download (3MB)
Official URL: http://repository.upi.edu

Abstract

Penelitian ini berhasil mensintesis nanopartikel Fe3O4@Au yang bersifat superparamagnetik dan biokompatibel untuk aplikasi pendeteksi logam berat. Sintesis dimulai dengan pembentukan inti magnetit (Fe3O4) menggunakan metode kopresipitasi, diikuti dengan pelapisan emas (Au) melalui metode sonokimia dengan reduksi ion emas dari prekursor HAuCl4 menggunakan gelombang ultrasonik. Karakterisasi menggunakan X-Ray Diffraction (XRD) mengidentifikasi struktur kristal kubik invers spinel, dengan fase primer Fe3O4 dan fase sekunder FeO(OH). Kurva histerisis menunjukkan nilai magnetisasi remanen (Mr) sebesar 5,38 emu/g, magnetisasi saturasi 37,94 emu/g, dan medan koersivitas 81,55 Oe. Particle Size Analyzer (PSA) menunjukkan ukuran rata-rata nanopartikel Fe3O4 sebesar 11,64 nm dengan PDI 0,35. SEM/EDS mengungkap mikrostruktur Fe3O4@Au dan mengkonfirmasi keberadaan Fe, Au, dan O. Spektroskopi UV-Vis menunjukkan puncak reflektansi maksimum sekitar 501-524 nm. Pengujian sensor menunjukkan rentang deteksi logam berat Ag dan Zn masing-masing sebesar 500 kΩ dan 18 kΩ. Hasil ini mengkonfirmasi keberhasilan sintesis dan potensi aplikasi nanopartikel Fe3O4@Au dalam pendeteksian logam berat. This study successfully synthesized superparamagnetic and biocompatible Fe3O4@Au nanoparticles for heavy metal detection applications. Synthesis began with the formation of a magnetite (Fe3O4) core using the coprecipitation method, followed by gold (Au) coating through a sonochemical method via reduction of gold ions from HAuCl4 precursor using ultrasonic waves. Characterization using X-Ray Diffraction (XRD) identified an inverse spinel cubic crystal structure, with primary phase Fe3O4 and secondary phase FeO(OH). The hysteresis curve showed a remanent magnetization (Mr) value of 5,38 emu/g, saturation magnetization of 37,94 emu/g, and coercivity of 81,55 Oe. Particle Size Analyzer (PSA) indicated an average Fe3O4 nanoparticle size of 11,64 nm with a PDI of 0,35. SEM/EDS revealed the microstructure of Fe3O4@Au and confirmed the presence of Fe, Au, and O. UV-Vis spectroscopy showed a maximum reflectance peak around 501-524 nm. Sensor testing indicated heavy metal detection ranges for Ag and Zn of 500 kΩ and 18 kΩ, respectively. These results confirm the successful synthesis and potential application of Fe3O4@Au nanoparticles in heavy metal detection.

Item Type: Thesis (S1)
Additional Information: https://scholar.google.com/citations?view_op=list_works&hl=en&user=nZJC-NoAAAAJ ID SINTA Dosen Pembimbing Ahmad Aminudin : 6002113
Uncontrolled Keywords: sintesis nanopartikel Fe3O4@Au, nanopartikel Fe3O4@Au, metode sonokimia, sensor logam berat. Fe3O4@Au nanoparticles synthesis, Fe3O4@Au nanoparticles, sonochemical method, heavy metal sensor
Subjects: L Education > L Education (General)
Q Science > QC Physics
Divisions: Fakultas Pendidikan Matematika dan Ilmu Pengetahuan Alam > Jurusan Pendidikan Fisika > Program Studi Fisika (non kependidikan)
Depositing User: Revanya Debora
Date Deposited: 07 Sep 2024 16:41
Last Modified: 07 Sep 2024 16:41
URI: http://repository.upi.edu/id/eprint/123469

Actions (login required)

View Item View Item