eprintid: 138633 rev_number: 26 eprint_status: archive userid: 217416 dir: disk0/00/13/86/33 datestamp: 2025-09-12 07:35:02 lastmod: 2025-09-12 07:35:02 status_changed: 2025-09-12 07:35:02 type: thesis metadata_visibility: show creators_name: Sherlla Dwinata, - creators_name: Andhy Setiawan, - creators_name: Eka Cahya Prima, - creators_nim: NIM2101638 creators_nim: NIDN0013107301 creators_nim: NIDN0026069001 creators_id: sherlladwn@upi.edu creators_id: andhys@upi.edu creators_id: ekacahyaprima@upi.edu contributors_type: http://www.loc.gov/loc.terms/relators/THS contributors_type: http://www.loc.gov/loc.terms/relators/THS contributors_name: Andhy Setiawan, - contributors_name: Eka Cahya Prima, - contributors_nidn: NIDN0013107301 contributors_nidn: NIDN0026069001 contributors_id: andhys@upi.edu contributors_id: ekacahyaprima@upi.edu title: PENGARUH KETEBALAN LAPISAN CsPbIBr₂ TERHADAP KINERJA SEL SURYA PEROVSKITE ispublished: pub subjects: Q1 subjects: QC divisions: FIS full_text_status: restricted keywords: CsPbIBr₂, Ketebalan lapisan perovskite, Sel surya perovskite. CsPbIBr₂, Perovskite layer thickness, Perovskite solar cell. note: https://scholar.google.com/citationshl=en&user=6UK8Q9kAAAAJ ID SINTA Dosen Pembimbing: Andhy Setiawan: 6040311 Eka Cahya Prima: 5977482 abstract: Sel surya perovskite memiliki prospek besar sebagai teknologi fotovoltaik generasi baru karena efisiensi tinggi dan proses fabrikasi sederhana, namun performanya masih dipengaruhi oleh stabilitas serta optimasi lapisan aktif. Penelitian ini bertujuan untuk menganalisis pengaruh variasi ketebalan lapisan perovskite CsPbIBr₂ terhadap sifat optik dan kinerja sel surya. Fabrikasi perangkat dilakukan dengan struktur FTO/TiO₂/CsPbIBr₂/Spiro-OMeTAD/Copper Tape. Variasi ketebalan diperoleh melalui metode layer by layer. Karakterisasi dilakukan menggunakan spektroskopi UV-Vis, pengukuran arus-tegangan (I–V), serta Scanning Electron Microscopy (SEM). Hasil UV-Vis menunjukkan bahwa peningkatan ketebalan lapisan meningkatkan absorbansi pada hampir seluruh panjang gelombang, dengan puncak serapan 300–350 nm. Kinerja sel surya terbaik diperoleh pada ketebalan 3 lapis dengan power conversion efficiency (PCE) 2,407 × 10⁻⁵ %, sementara nilai short-circuit current density (Jsc) tertinggi terdapat pada ketebalan 5 lapis sebesar 0,026 mA/cm². Ketebalan berlebih (7 dan 9 lapis) menurunkan performa akibat jarak transport muatan lebih panjang dan peluang rekombinasi lebih tinggi. Analisis SEM mengonfirmasi bahwa film 3 lapis memiliki morfologi kristal vertikal dengan ketebalan sekitar 250 nm, yang mendukung transport muatan dan mengurangi rekombinasi non-radiatif. Perovskite solar cells have attracted considerable attention as a next-generation photovoltaic technology due to their high efficiency and simple fabrication process. However, their performance is strongly affected by stability issues and optimization of the active layer structure. This study aims to investigate the effect of perovskite CsPbIBr₂ layer thickness on the optical properties and performance of the solar cell. The device was fabricated with the structure FTO/TiO₂/CsPbIBr₂/SpiroOMeTAD/Copper Tape. The thickness variation was controlled using the layer by layer method. Characterization techniques included UV-Vis spectroscopy, current– voltage (I–V) measurements, and Scanning Electron Microscopy (SEM). UV-Vis results showed that increasing film thickness enhanced the absorbance across most wavelengths, with a strong absorption peak observed at 300–350 nm. The best photovoltaic performance was obtained at 3 layers, yielding a power conversion efficiency (PCE) of 2.407 × 10⁻⁵ %, while the highest short-circuit current density (Jsc) of 0.026 mA/cm² was observed at 5 layers. Excessive thicknesses (7 and 9 layers) led to performance degradation due to longer carrier transport distances and higher recombination probability. SEM analysis confirmed that the 3-layer film had a vertical crystal orientation with ~250 nm thickness, supporting efficient charge transport and reducing non-radiative recombination. date: 2025-08-28 date_type: published institution: Universitas Pendidikan Indonesia department: KODEPRODI45201#Fisika_S1 thesis_type: other thesis_name: other official_url: https://repository.upi.edu/ related_url_url: https://perpustakaan.upi.edu/ related_url_type: org citation: Sherlla Dwinata, - and Andhy Setiawan, - and Eka Cahya Prima, - (2025) PENGARUH KETEBALAN LAPISAN CsPbIBr₂ TERHADAP KINERJA SEL SURYA PEROVSKITE. S1 thesis, Universitas Pendidikan Indonesia. document_url: http://repository.upi.edu/138633/1/S_FIS_2101638_Title.pdf document_url: http://repository.upi.edu/138633/2/S_FIS_2101638_Chapter1.pdf document_url: http://repository.upi.edu/138633/3/S_FIS_2101638_Chapter2.pdf document_url: http://repository.upi.edu/138633/6/S_FIS_2101638_Chapter3.pdf document_url: http://repository.upi.edu/138633/4/S_FIS_2101638_Chapter4.pdf document_url: http://repository.upi.edu/138633/5/S_FIS_2101638_Chapter5.pdf document_url: http://repository.upi.edu/138633/7/S_FIS_2101638_Appendix.pdf