TY  - THES
Y1  - 2025/08/28/
UR  - https://repository.upi.edu/
KW  - DSSC
KW  -  Average Transmittance Visible
KW  -  Light Utilization Efficiency
KW  - 
TiO?
KW  -  Transparansi
N1  - ID Sinta Dosen Pembimbing:
Eka Cahya Prima: 5977482
Wilman Septina: 6860191
N2  - Penelitian ini berfokus pada pengembangan Dye Sensitized Solar Cell (DSSC) semitransparan yang memerlukan keseimbangan antara efisiensi konversi daya dan transparansi optik. Rumusan masalah yang dikaji adalah pengaruh optimasi pasta TiO? terhadap karakteristik fotoelektroda dan kinerja DSSC semitransparan, serta pengaruh kombinasi organik dye terhadap kinerjanya. Tujuan penelitian ini adalah menganalisis variasi pasta TiO? komersial, jenis dye, dan waktu loading dye terhadap parameter efisiensi (PCE), Average Visible Transmittance (AVT), dan Light Utilization Efficiency (LUE). Metode yang digunakan meliputi pembuatan fotoelektroda dengan pasta TiO? (18NR-AO, 90T, dan 18NR-T), uji variasi dye organik (Y123, XY1B, dan campuran 1:1), serta optimasi waktu loading dye pada konfigurasi satu lapis dan dua lapis. Karakterisasi dilakukan menggunakan pengukuran kurva J?V dan transmitansi optik. Hasil menunjukkan bahwa pasta 90T memberikan performa paling seimbang untuk DSSC semitransparan, dengan PCE 3,99%, AVT 11,41%, dan LUE 0,5%, lebih unggul dibandingkan 18NR-T. Variasi dye menunjukkan Y123 dua lapis menghasilkan AVT dan LUE tertinggi. Pada optimasi waktu loading, konfigurasi satu lapis TiO? dengan 24 jam loading dye Y123 menghasilkan transparansi tertinggi AVT 33,74%, LUE 1,54% meskipun PCE sedikit lebih rendah 4,57% dibanding 12 jam. Secara keseluruhan, hasil ini menegaskan adanya trade-off antara efisiensi dan transparansi, dengan kondisi 24 jam sebagai kompromi terbaik untuk aplikasi DSSC semitransparan. Penelitian ini dilakukan di Pusat Riset Elektronika, Badan Riset dan Inovasi Nasional (BRIN), dari bulan Februari hingga Juli.

This study focuses on the development of semitransparent Dye-Sensitized Solar Cells (DSSC), aiming to balance power conversion efficiency and optical transparency. The research investigates the effect of TiO? paste optimization and organic dye combinations on the performance of semitransparent DSSC. The objective is to analyze the impact of TiO? paste variations, dye types, and loading times on efficiency parameters (PCE), Average Visible Transmittance (AVT), and Light Utilization Efficiency (LUE). Methods include preparing photoelectrodes with TiO? pastes (18NR-AO, 90T, and 18NR-T), testing organic dye variations (Y123, XY1B, and 1:1 mixture), and optimizing dye loading times in single and double layers. Characterization was performed using J-V curves and optical transmittance measurements. The results show that 90T paste provides the best performance, with a PCE of 3.99%, AVT of 11.41%, and LUE of 0.5%. Y123 dye in a two-layer configuration achieves the highest AVT and LUE. Optimizing loading time, the 24-hour Y123 dye loading with single-layer TiO? yielded the highest AVT (33.74%) and LUE (1.54%), with a slightly lower PCE of 4.57%. These results highlight the trade-off between efficiency and transparency, with 24 hours being the optimal compromise for semitransparent DSSC applications.
This research was conducted at the Electronics Research Center, National Research and Innovation Agency (BRIN), from February to July.
AV  - restricted
TI  - OPTIMASI KARAKTERISTIK FOTOELEKTRODA TiO2 PADA DYE SENSITIZED SOLAR CELL UNTUK APLIKASI SEL SURYA TRANSPARAN
A1  - Muhammad Nur Al Araf, -
A1  - Eka Cahya Prima, -
A1  - Wilman Septina, -
ID  - repoupi137105
M1  - other
PB  - Universitas Pendidikan Indonesia
ER  -