title: OPTIMASI KARAKTERISTIK FOTOELEKTRODA TiO2 PADA DYE SENSITIZED SOLAR CELL UNTUK APLIKASI SEL SURYA TRANSPARAN
creator: Muhammad Nur Al Araf, -
creator: Eka Cahya Prima, -
creator: Wilman Septina, -
subject: QC Physics
subject: QD Chemistry
subject: TK Electrical engineering. Electronics Nuclear engineering
description: Penelitian ini berfokus pada pengembangan Dye Sensitized Solar Cell (DSSC) semitransparan yang memerlukan keseimbangan antara efisiensi konversi daya dan transparansi optik. Rumusan masalah yang dikaji adalah pengaruh optimasi pasta TiO₂ terhadap karakteristik fotoelektroda dan kinerja DSSC semitransparan, serta pengaruh kombinasi organik dye terhadap kinerjanya. Tujuan penelitian ini adalah menganalisis variasi pasta TiO₂ komersial, jenis dye, dan waktu loading dye terhadap parameter efisiensi (PCE), Average Visible Transmittance (AVT), dan Light Utilization Efficiency (LUE). Metode yang digunakan meliputi pembuatan fotoelektroda dengan pasta TiO₂ (18NR-AO, 90T, dan 18NR-T), uji variasi dye organik (Y123, XY1B, dan campuran 1:1), serta optimasi waktu loading dye pada konfigurasi satu lapis dan dua lapis. Karakterisasi dilakukan menggunakan pengukuran kurva J–V dan transmitansi optik. Hasil menunjukkan bahwa pasta 90T memberikan performa paling seimbang untuk DSSC semitransparan, dengan PCE 3,99%, AVT 11,41%, dan LUE 0,5%, lebih unggul dibandingkan 18NR-T. Variasi dye menunjukkan Y123 dua lapis menghasilkan AVT dan LUE tertinggi. Pada optimasi waktu loading, konfigurasi satu lapis TiO₂ dengan 24 jam loading dye Y123 menghasilkan transparansi tertinggi AVT 33,74%, LUE 1,54% meskipun PCE sedikit lebih rendah 4,57% dibanding 12 jam. Secara keseluruhan, hasil ini menegaskan adanya trade-off antara efisiensi dan transparansi, dengan kondisi 24 jam sebagai kompromi terbaik untuk aplikasi DSSC semitransparan. Penelitian ini dilakukan di Pusat Riset Elektronika, Badan Riset dan Inovasi Nasional (BRIN), dari bulan Februari hingga Juli.    This study focuses on the development of semitransparent Dye-Sensitized Solar Cells (DSSC), aiming to balance power conversion efficiency and optical transparency. The research investigates the effect of TiO₂ paste optimization and organic dye combinations on the performance of semitransparent DSSC. The objective is to analyze the impact of TiO₂ paste variations, dye types, and loading times on efficiency parameters (PCE), Average Visible Transmittance (AVT), and Light Utilization Efficiency (LUE). Methods include preparing photoelectrodes with TiO₂ pastes (18NR-AO, 90T, and 18NR-T), testing organic dye variations (Y123, XY1B, and 1:1 mixture), and optimizing dye loading times in single and double layers. Characterization was performed using J-V curves and optical transmittance measurements. The results show that 90T paste provides the best performance, with a PCE of 3.99%, AVT of 11.41%, and LUE of 0.5%. Y123 dye in a two-layer configuration achieves the highest AVT and LUE. Optimizing loading time, the 24-hour Y123 dye loading with single-layer TiO₂ yielded the highest AVT (33.74%) and LUE (1.54%), with a slightly lower PCE of 4.57%. These results highlight the trade-off between efficiency and transparency, with 24 hours being the optimal compromise for semitransparent DSSC applications.  This research was conducted at the Electronics Research Center, National Research and Innovation Agency (BRIN), from February to July.
date: 2025-08-28
type: Thesis
type: NonPeerReviewed
format: text
language: id
identifier: http://repository.upi.edu/137105/1/S_FIS_2100979_Title.pdf
format: text
language: id
identifier: http://repository.upi.edu/137105/2/S_FIS_2100979_Chapter1.pdf
format: text
language: id
identifier: http://repository.upi.edu/137105/3/S_FIS_2100979_Chapter2.pdf
format: text
language: id
identifier: http://repository.upi.edu/137105/4/S_FIS_2100979_Chapter3.pdf
format: text
language: id
identifier: http://repository.upi.edu/137105/5/S_FIS_2100979_Chapter4.pdf
format: text
language: id
identifier: http://repository.upi.edu/137105/6/S_FIS_2100979_Chapter5.pdf
format: text
language: id
identifier: http://repository.upi.edu/137105/7/S_FIS_2100979_Appendix.pdf
identifier:   Muhammad Nur Al Araf, - and Eka Cahya Prima, - and Wilman Septina, -  (2025) OPTIMASI KARAKTERISTIK FOTOELEKTRODA TiO2 PADA DYE SENSITIZED SOLAR CELL UNTUK APLIKASI SEL SURYA TRANSPARAN.  S1 thesis, Universitas Pendidikan Indonesia.   
relation: https://repository.upi.edu/