ISOLASI SELULOSA NANOKRISTALIN DARI BIOMASSA BATANG PISANG MENGGUNAKAN CAIRAN IONIK CIS-OLEIL IMIDAZOLINIUM ASETAT

Effendi, Devi Bentia (2015) ISOLASI SELULOSA NANOKRISTALIN DARI BIOMASSA BATANG PISANG MENGGUNAKAN CAIRAN IONIK CIS-OLEIL IMIDAZOLINIUM ASETAT. S1 thesis, Universitas Pendidikan Indonesia.

[img]
Preview
Text
S_KIM_1002368_Title.pdf

Download (148kB) | Preview
[img]
Preview
Text
S_KIM_1002368_Abstract.pdf

Download (336kB) | Preview
[img]
Preview
Text
S_KIM_1002368_Table_of_content.pdf

Download (303kB) | Preview
[img]
Preview
Text
S_KIM_1002368_Chapter1.pdf

Download (225kB) | Preview
[img] Text
S_KIM_1002368_Chapter2.pdf
Restricted to Staf Perpustakaan

Download (759kB)
[img]
Preview
Text
S_KIM_1002368_Chapter3.pdf

Download (361kB) | Preview
[img] Text
S_KIM_1002368_Chapter4.pdf
Restricted to Staf Perpustakaan

Download (1MB)
[img]
Preview
Text
S_KIM_1002368_Chapter5.pdf

Download (67kB) | Preview
[img]
Preview
Text
S_KIM_1002368_Bibliography.pdf

Download (154kB) | Preview
Official URL: http://repository.upi.edu/

Abstract

Penelitian ini bertujuan untuk mendapatkan partikel material selulosa nanokristalin menggunakan cairan ionik dengan metode yang sederhana, murah, dan ramah lingkungan. Bahan utama yang digunakan adalah limbah batang pisang sebagai sumber selulosa dan cairan ionik cis-oleil imidazolinium asetat sebagai katalis. Metode yang dilakukan pada penelitian ini adalah sintesis cairan ionik, preparasi biomassa batang pisang dan isolasi selulosa nanokristalin. Hasil karakterisasi dari sintesis cairan ionik menggunakan FTIR dan NMR menunjukkan bahwa cairan ionik cis-oleil imidazolinium asetat pada penelitian kali ini telah berhasil disintesis. Hasil FTIR dari selulosa hasil isolasi menunjukkan jenis selulosa II yang artinya distribusi interaksi ikatan hidrogen telah teratur yang terlihat pada ikatan O2(O no.2)-O6(O no.6). Hasil XRD dari selulosa hasil isolasi terdapat puncak khas pada 2θ=20.1 yang mengindikasikan selulosa nanokristalin. Hasil TG-DTA menunjukkan adanya penurunan kestabilan termal yang menandakan pertambahan luas permukaan, hal tersebut mengindikasikan bahwa filtrat selulosa hasil isolasi merupakan selulosa berukuran nano. Hasil SEM menunjukkan adanya perubahan ukuran partikel dari selulosa setelah tahap isolasi. Hasil TEM menunjukkan ukuran selulosa dengan panjang ±330 nm dan lebar ±54 nm pada kondisi optimum dengan daya 100W selama 30 menit. This research was aimed to obtain the nanocrystalline cellulose particles used an ionic liquid as catalytic agent with a simple, inexpensive, and environmental friendly methods. The resources of cellulose in this research was banana stem gained from domestic waste. For the catalytic agent, we used cis-oleil imidazolinium acetate ionic liquids. The methods was synthesis of ionic liquids, preparation of banana stem, and nanocrystalline cellulose isolation. The FTIR and NMR results for synthesis of ionic liquids shows the cis-oleil imidazolinium acetate ionic liquids in this research was succesfully synthesized. The FTIR results of celluose after treatment shows cellulose type II, which means the distribution of hydrogen bonding interactions have regularly seen on O2(O no.2)-O6(O no.6) bond. The XRD results of cellulose after treatment shows the peak at 2θ=20.1 that indicates of nanocrystalline cellulose. The TG-DTA results shows a decreasing in thermal stability which indicates the increase of surface area and shows that filtrate cellulose after treatment are nano-sized. The SEM results shows a change in the particles size of the cellulose after isolation step. The TEM results shows the particles size of the cellulose with length ±330 nm and diameter ±54 nm in optimum condition at 100W for 30 minutes.

Item Type: Skripsi Tesis Atau Disertasi (S1)
Additional Information: No. Panggil: S KIM EFF i-2015; Pembimbing: I. Ahmad Mudzakir, II. Eng. Asep Bayu Dani Nandiyanto
Uncontrolled Keywords: Selulosa Nanokristalin, Batang Pisang, Cairan Ionik, Fatty Imidazolinium
Subjects: Q Science > QD Chemistry
Divisions: Fakultas Pendidikan Matematika dan Ilmu Pengetahuan Alam > Jurusan Pendidikan Kimia > Program Studi Kimia (non kependidikan)
Depositing User: Staf Koordinator 3
Date Deposited: 16 Sep 2015 02:44
Last Modified: 16 Sep 2015 02:44
URI: http://repository.upi.edu/id/eprint/16902

Actions (login required)

View Item View Item