DURABILITAS BETON DENGAN BAHAN TAMBAH SILICA FUME DI LINGKUNGAN AIR LAUT

Bagas Somantri, - (2024) DURABILITAS BETON DENGAN BAHAN TAMBAH SILICA FUME DI LINGKUNGAN AIR LAUT. S1 thesis, Universitas Pendidikan Indonesia.

[img] Text
S_TS_2005868_Title.pdf

Download (10MB)
[img] Text
S_TS_2005868_Chapter1.pdf

Download (10MB)
[img] Text
S_TS_2005868_Chapter2.pdf
Restricted to Staf Perpustakaan

Download (10MB)
[img] Text
S_TS_2005868_Chapter3.pdf

Download (10MB)
[img] Text
S_TS_2005868_Chapter4.pdf
Restricted to Staf Perpustakaan

Download (10MB)
[img] Text
S_TS_2005868_Chapter5.pdf

Download (10MB)
[img] Text
S_TS_2005868_Appendix.pdf
Restricted to Staf Perpustakaan

Download (10MB)
Official URL: https://repository.upi.edu/

Abstract

Elemen struktur bangunan di pantai atau laut banyak yang menggunakan beton. Air laut adalah salah satu penyebab kegagalan pada struktur bangunan. Intrusi air laut dapat memberikan efek yang merugikan untuk komponen struktural konstruksi. Kondisi ini membutuhkan beton yang kedap air dan keawetan (durability) yang baik. Salah satu bahan tambah yang bisa digunakan untuk memperbaiki sifat beton adalah silica fume. Penelitian ini bertujuan untuk mengetahui pengaruh bahan tambah silica fume terhadap durabilitas beton di lingkungan air laut. Benda uji dibuat dengan beton rencana f’c = 30 MPa sebagai kontrol dan dilakukan perawatan dengan air tawar dan air laut. Metode yang digunakan adalah metode eksperimen. Hasil pengujian slump mengalami penurunan dengan nilai slump beton kontrol yaitu 9,5 cm. Pada beton silica fume dengan variasi 3%, 6%, 9%, 12% dan 15% nilai slump menurun secara berurutan yaitu 8,9 cm; 8,1 cm; 6,8 cm; 6,3 cm; 5,8 cm. Hasil penelitian menunjukkan kuat tekan beton kontrol 0% umur 56 hari pada curing air laut yaitu 26,59 MPa dan pada curing air tawar yaitu 31,36 MPa, beton variasi silica fume umur 56 hari memiliki nilai kuat tekan rata-rata berturut-turut dari variasi paling rendah adalah 30,32 MPa; 32,40 MPa; 31,51 MPa; 30,99 MPa dan 28,65 MPa pada curing air laut serta 31,87 MPa; 35,41 MPa; 36,10 MPa; 33,48 MPa dan 31,58 MPa pada curing air tawar. Hasil tersebut menunjukkan kuat tekan maksimum terjadi pada variasi bahan tambah silica fume sebesar 6% di rendaman air laut dan 9% di rendaman air tawar. Many structural elements of buildings on the beach or sea use concrete. Sea water is one of the causes of failure in building structures. Seawater intrusion can have detrimental effects on structural components of construction. This condition requires concrete that is waterproof and has good durability. One additional material that can be used to improve the properties of concrete is silica fume. This research aims to determine the effect of added silica fume on the durability of concrete in a sea water environment. The test specimens were made with concrete designed for f'c = 30 MPa as a control and treated with fresh water and sea water. The method used is the experimental method. The slump test results decreased with the control concrete slump value being 9.5 cm. In silica fume concrete with variations of 3%, 6%, 9%, 12% and 15%, the slump value decreases sequentially, namely 8.9 cm; 8.1cm; 6.8cm; 6.3cm; 5.8 cm. The results of the research show that the compressive strength of the 0% control concrete aged 56 days in seawater curing is 26.59 MPa and in freshwater curing, namely 31.36 MPa, the silica fume variation concrete aged 56 days has an average compressive strength value respectively from the lowest variation is 30.32 MPa; 32.40 MPa; 31.51 MPa; 30.99 MPa and 28.65 MPa in sea water curing and 31.87 MPa; 35.41 MPa; 36.10 MPa; 33.48 MPa and 31.58 MPa in fresh water curing. The results showed a strong maximum pressure occurred on the variation of silica fume additives of 6% on seawater immersions and 9% on freshwater immersions.

Item Type: Thesis (S1)
Additional Information: https://scholar.google.com/citations?view_op=new_articles&hl=en&imq=Bagas+Somantri# ID SINTA Dosen Pembimbing: Istiqomah: 6000414 Nanang Dalil Herman: 6040771
Uncontrolled Keywords: Durabilitas Beton, Silica Fume, Air Laut, Kuat Tekan Concrete Durability, Silica Fume, Sea Water, Compressive Strength
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Divisions: Fakultas Pendidikan Teknik dan Industri > Jurusan Pendidikan Teknik Sipil > Program Studi Teknik Sipil
Depositing User: Bagas Somantri
Date Deposited: 11 Oct 2024 08:07
Last Modified: 11 Oct 2024 08:07
URI: http://repository.upi.edu/id/eprint/127273

Actions (login required)

View Item View Item