SINTESIS ZEOLIT BERBASIS ABU TERBANG YANG DIMODIFIKASI SENG OKSIDA UNTUK ADSORPSI ANTIBIOTIK KLINDAMISIN

Jessica Veronica, - (2023) SINTESIS ZEOLIT BERBASIS ABU TERBANG YANG DIMODIFIKASI SENG OKSIDA UNTUK ADSORPSI ANTIBIOTIK KLINDAMISIN. S1 thesis, Universitas Pendidikan Indonesia.

	Text S_KIM_1903900_Title.pdf Download (2MB)
	Text S_KIM_1903900_Chapter1.pdf Download (2MB)
	Text S_KIM_1903900_Chapter2.pdf Restricted to Staf Perpustakaan Download (2MB)
	Text S_KIM_1903900_Chapter3.pdf Download (2MB)
	Text S_KIM_1903900_Chapter4.pdf Restricted to Staf Perpustakaan Download (2MB)
	Text S_KIM_1903900_Chapter5.pdf Download (2MB)
	Text S_KIM_1903900_Appendix.pdf Restricted to Staf Perpustakaan Download (2MB)

Abstract

Klindamisin merupakan antibiotik yang banyak digunakan dalam bidang medis setiap tahunnya dan menjadi kontaminan di perairan. Salah satu metode yang efektif untuk mengatasi kontaminasi klindamisin, yaitu adsorpsi. Abu terbang atau fly ash (FA) merupakan limbah batu bara yang sebagian besar berasal dari industri tekstil dengan tingkat daur ulang yang rendah sehingga banyak digunakan sebagai adsorben. Penelitian ini bertujuan untuk mendapatkan zeolit berbasis FA yang dimodifikasi seng oksida (ZFA-ZnO) untuk mengadsorpsi antibiotik klindamisin. Metode yang digunakan dalam penelitian ini, yaitu sintesis hidrotermal dengan autoclave untuk mendapatkan ZFA-ZnO dan pengujian adsorpsi menggunakan sistem batch. ZFA-ZnO dikarakterisasi lebih lanjut menggunakan X-ray Diffraction (XRD), Fourier Transform Infrared (FTIR), dan pengujian adsorpsi dilakukan menggunakan instrumen spektrofotometer Ultraviolet-Visible (UV-Vis). Berdasarkan hasil karakterisasi menggunakan XRD, didapatkan keadaan sintesis paling optimum, yaitu pada suhu 160oC selama 9 jam yang ditunjukkan dengan meningkatnya fasa kristalin zeolit dan bertambahnya puncak ZnO. ZFA-ZnO magnetik pada suhu 160oC (ZFA-ZnO160 M) merupakan jenis zeolit dengan persentase adsorpsinya paling tinggi, yaitu sebesar 89,41%. Data adsorpsi menunjukkan bahwa pH optimum untuk mengadsorpsi antibiotik klindamisin, yaitu pH 6 dengan persentase adsorpsi untuk ZFA160 M sebesar 82,43% dan ZFA-ZnO160 M sebesar 94,5%. Data isoterm adsorpsi untuk ZFA160 M paling sesuai dengan model Langmuir dengan regresi kuadrat 0,98837 dan chi kuadrat 0,24054. Sedangkan untuk ZFA-ZnO160 M, data adsorpsi sesuai dengan model isoterm Redlich Peterson dengan regresi kuadrat 0,99674 dan chi kuadrat 0,07293. Mekanisme adsorpsi diduga berlangsung secara monolayer melalui interaksi pada gugus fungsi aktif pada zeolit, yaitu Si-O, hasil diperkuat dengan analisis serapan gugus fungsi pada FTIR. Clindamycin is an antibiotic that is widely used in the medical field every year and is a contaminant in waters. One effective method for dealing with clindamycin contamination is adsorption Fly ash (FA) is coal waste which mostly comes from the textile industry with a low recycling rate so it is widely used as an adsorbent. This study aims to obtain FA-based zeolite modified by zinc oxide (ZFA-ZnO) to adsorb the antibiotic clindamycin. The method used in this study was hydrothermal synthesis with an autoclave to obtain ZFA-ZnO and the batch system was used for adsorption testing. ZFA-ZnO was further characterized using X-ray Diffraction (XRD), Fourier Transform Infrared (FTIR), and adsorption tests were carried out using an Ultraviolet-Visible (UV-Vis) spectrophotometer. Based on the results of the characterization using XRD, the optimum synthesis conditions were obtained, namely at 160oC for 9 hours as indicated by an increase in the zeolite crystalline phase and an increase in the ZnO peak. Magnetic ZFA-ZnO at a temperature of 160oC (ZFA-ZnO160 M) was a type of zeolite with the highest adsorption percentage, namely 89.41%. Adsorption data showed that the optimum pH for adsorbing clindamycin antibiotics was pH 6 with an adsorption percentage for ZFA160 M of 82.43% and ZFA-ZnO160 M of 94.5%. The adsorption isotherm data for ZFA160 M best fits the Langmuir model with a quadratic regression of 0.98837 and a chi square of 0.24054. Meanwhile for ZFA-ZnO160 M, the adsorption data is in accordance with the Redlich Peterson isotherm model with a quadratic regression of 0.99674 and a chi square of 0.07293. The adsorption mechanism is thought to take place in a monolayer manner through the interaction of the active functional groups in the zeolite, namely Si-O, the results are confirmed by functional group absorption analysis on FTIR.

Item Type:	Thesis (S1)
Additional Information:	Link Google Scholar: https://scholar.google.com/citations?hl=en&user=fKITsq8AAAAJ ID SINTA Dosen Pembimbing: Galuh Yuliani : 5975260 Abraham Mora : 6778862
Uncontrolled Keywords:	ZFA-ZnO, magnetic, adsorpsi, klindamisin, zeolit
Subjects:	L Education > L Education (General)
Divisions:	Fakultas Pendidikan Matematika dan Ilmu Pengetahuan Alam > Jurusan Pendidikan Kimia > Program Studi Kimia (non kependidikan)
Depositing User:	Jessica Veronica
Date Deposited:	25 Sep 2023 08:36
Last Modified:	25 Sep 2023 08:36
URI:	http://repository.upi.edu/id/eprint/108135

Actions (login required)

View Item